Community prints.

Was fairly decent for not tweaking any of the settings, there was warping on all corners however, and there was some weirdness going on between the wave and standard layers. Printed with Sunlu PLA on a Voron 2.4 with an A4T toolhead.

by Ice

More warping than last ABS sample, might be caused by me opening the enclosure during the wave section.

by Rob

Low amount of warping, small amount of lifting near the smaller wave section.

by Rob

Slightly better than last ABS print. Least warping so far.

by Rob

Line spacing a tad bit too much. Layers are seperating. Only slight warping. Ends of the smaller waves stick out again.

by Rob

Slight warping, noticed some curling on individual layers near the smaller waves.

by Rob

Good adhesion, some gaps between the waves and perimeter. Slight warping

by Rob

Very good adhesion between layers. Slight warping, not quite perfect.

by Rob

Good result, only there is a lot of warping present.

by Rob

Line spacing increased too much. Interlayer adhesion is suffering.

by Rob

The first overhang layer looked great, but once printing of the next layer started, the first one got bent downwards. Probably, there were some blobs protruding upwards from the first overhang layer, which then got caught by the nozzle, pushing the whole first layer down.

Looking really good, still a lot of warping.

by Rob

Huge step back from the last ABS print. Looks like underextrusion, will try higher wave flow next.

by Rob

Only problem with this print is the amount of warping observed.

by Rob

Better than the other PHA samples, but still not good enough. PHA warps in a completely different way than the other materials, PHA might not be suitable using the wave overhangs.

by Rob

On the flange the gaps between the holes and the edge are too small to wave through. Some warping also.

by ja

Shape is there, messed up on the perimeter. Material warps a lot even though it looks like it shouldnt.

by Rob

Not good at all, seems like the waves do not adhere to each other.

by Rob

good+... relatively low warping. Has gaps on straight sections and smaller features show consequences of warping. The large curve is near perfect

by Tawpie

Default settings

Still not good, very similar to last PHA sample.

by Rob

Line spacing might be too high, as the adhesion between layers is suffering (Classic ABS). Might be that this is printed in an open printer, will try later in an enclosed one. Warping is definitely less than the other ABS sample.

by Rob

It is getting there, still testing settings.

by Rob

First time ABS, printed in open air on the BBL A1 Mini. Layer adhesion is very good, only in the extremities there is some artifacting. Warps a lot though

by Rob

Failed, not sure why yet exactly

by Rob

It is getting there, on the good parts of the print, the curling is extreme

by Rob

Not a lot to say for this one

by Rob

Does not look well at all. It looks like a fly got stuck between two of the layers. Don't know exactly what needs changing yet.

by Rob

by Zevilbofh

by Dennis

Even slower does not really seem to matter

by Dennis

Results seem slightly better with the slower layers ontop of the overhang layer

by Dennis

Too much.

by Rob

Even more warping caused by the line spacing.

by Rob

Increased the line spacing too much, warping as a result of it.

by Rob

Tried to mitigate the gaps by increasing the perimeter overlap. Might be the best sample so far. Waves are good and adhere well with each other.

by Rob

Even bigger gaps near the perimeter, starting to become a problem especially in the inner corner. Waves once again look nice

by Rob

Bigger gaps starting to form near the perimeter due to line spacing. Waves look nice

by Rob

Print overall is very good, slight warping in the overhang caused some overextrusion in subsequent layers.

by Rob

Hilbert floor + 30% fan (vs 100% default). Thought slower cooling reduces stress lock-in. However, it warped worse, not better. Hot floor likely sagged into and pulled on the wave during its longer cooldown

by Dennis

Even for cases that can be printed with bridges, result might be better with waveoverhangs.

by Dennis

60% vs 100% Hilbert curve did not seem to make a difference

by Dennis

First test with Hilbert-curve settings (https://github.com/dennisklappe/OrcaSlicer-WaveOverhangs/pull/34), definitely some less warping. Will do some more tests and also compare to just no top-layers at all. Will release this later today.

by Dennis

Tested corner-aware spacing taper (https://github.com/dennisklappe/OrcaSlicer-WaveOverhangs/pull/29) on the small corner, need some more testing to see it's usefulness.

by Dennis

by Dennis

by Dennis

by ruether

I get an error saying vector too long when i try to slice. i cant even get to the point where i try to physically print the model. I have provided the 3mf file so hopefully it'll help you all debug this.

Not quite perfect, quite a bit of warping in the extremities. Between a 4 and 5 I would say

by Rob

Even better than last sample. Warping only near the smaller wave segments but minimal. Tuning line spacing such that there is barely the adhesion to suspend the material mid air might give the best results. However, there are gaps starting to form near the perimeter as a result of the line spacing.

by Rob

Very good sample, increased the line spacing to above 0.4 to 0.42. The only issue on this sample is the warping in the area with concentrated waves.

by Rob

Small amount of layer separation, as seen in photo 2. Minimal warping, only near the smaller waves. On the top side, the waves and perimeter do not properly connect, but can already be seen in the gcode viewer.

by Rob

Not a lot of warping, though there are some spots where there are gaps between tracks and the perimeter (See photo 2).

by Rob

Better overall compared to the last. Warping similar to last as well. The rough surface is less than before.

by Rob

Adhesion between base and overhang weak, line spacing causing issues near perimeter. Warping is less than last sample.

by Rob

The connection between the base of the model and the wave overhang is weak. A wavy pattern can be identified on the bottom and top surface again. Significant warping again

by Rob